2026-06-18 216576 H2O_10-8mbar.csv 2026-06-18 2026-06-18 113584 CO2_mbar.csv CO2_mbar.csv 2026-06-18 2026-06-18 386699 H2O_10-4mbar.csv 2026-06-18 ICU = ICMM oai:digital.csic.es:10261/396904 OAI-PMH OAI text/csv txt 2026-06-18 2026-06-18 99018 H2O_mbar.csv 2026-06-18 2026-06-18 441210 H2O_10-6mbar.csv 2026-06-18 2026-06-18 BM25-SpLine beamline BM25-SpLine beamline Source data for Figures 2, 3 and 4 of the article entitled "Phase stability of iron oxides epitaxial thin films under O₂, CO₂ and H₂O environmental conditions", J. Mater. Chem. C, 2025. Datos de origen para las Figuras 2, 3 y 4 del artículo titulado "La estabilidad de los óxidos de hierro en las películas delgadas epitaxiales bajo condiciones ambientales O2, CO2 y H2O", J. Mater. Chem. C, 2025. (Traducción automática) http://hdl.handle.net/10261/396904 info:eu-repo/semantics/dataset [Descripción de los métodos de reunión de datos] In-situ Grazing Incidence X-ray Diffraction (GIXRD) se realizó en la línea BM25-SpLine del ESRF. Se realizaron mediciones durante el acaparamiento bajo O2, CO2, H2O y UHV, con temperaturas que oscilan entre RT y 1100°C y presiones de 10−9 mbar a 1 bar. Las películas se cultivaron epitaxialmente en sustratos SrTiO3(001). (Traducción automática) [Description of data collection methods] In-situ Grazing Incidence X-ray Diffraction (GIXRD) was performed at the BM25-SpLine beamline at the ESRF. Measurements were carried out during annealing under O₂, CO₂, H₂O and UHV, with temperature ranging from RT to 1100°C and pressures from 10⁻⁹ mbar to 1 bar. Films were epitaxially grown on SrTiO₃(001) substrates. 2024-08-05 conforme-DCAT-AP-ES 2026-06-18 64129 CO2_10-8mbar.csv CO2_10-8mbar.csv 2026-06-18 2026-06-18 156517 O2_10-6mbar.csv 2026-06-18 2026-06-18 122987 CO2_bar.csv CO2_bar.csv 2026-06-18 Digital.CSIC Agencia Estatal Consejo Superior de Investigaciones Científicas 2026-06-18 133558 O2_10-8mbar.csv 2026-06-18 2026-06-18 110306 O2_10-4mbar.csv 2026-06-18 2026-06-18 161811 CO2_10-4mbar.csv CO2_10-4mbar.csv 2026-06-18 2026-06-18 4385 DIGITAL_CSIC_README_Phase_stability_iron_oxides_epitaxial_Sebastiani_Tofano.txt 2026-06-18 2024-08-05 2026-06-18 101719 CO2_10-6mbar.csv CO2_10-6mbar.csv 2026-06-18 DIGITAL.CSIC 2026-06-22T11:33:48.182067+02:00 2026-06-22T19:00:21.734966+02:00 Agencia Estatal Consejo Superior de Investigaciones Científicas EA0041268 2026-06-18 87587 UHV.csv 2026-06-18 2026-06-18 68426 O2_1mbar.csv 2026-06-18